In this study, durian shell-based activated carbon (DAC) was produced via chemical activation method by utilising durian shell and sulphuric acid (H2SO4) as the starting material and activating agent, respectively. The incorporation of H2SO4 in the DAC production process resulted an improvement in the surface properties and adsorption capacity of the produced DAC adsorbent. Field emission scanning electron microscopy analysis further showed that the produced DAC possessed a porous structure which was beneficial for dye adsorption application. Under operating conditions of 500°C and 3 hours carbonisation temperature and time, the Brunauer–Emmett–Teller (BET) surface area, total pore volume and BET average pore diameter were measured to be 242.03 m2/g, 0.028 cm3/g and 2.28 nm, respectively. The adsorption performance of the produced DAC was then investigated using methylene blue (MB) as the model adsorbate. The optimum MB dye removal and adsorption capacity were found to be 92.05% a.....

165 hits

The development of scalable membrane-based separation processes has attracted considerable interest on laboratory and industrial scales. Polyvinylidene fluoride (PVDF) is one of the most widely used fluoropolymer materials for membrane fabrication due to its excellent mechanical strength, good thermal stability and chemical resistance as well as aging resistance. However, the hydrophobic nature of PVDF has resulted in serious membrane fouling during the filtration process. From the past decade, the embedment of hydrophilic materials in/on PVDF-based membranes can significantly alter the membrane’s morphology and surface properties. Therefore, based on most articles retrieved from Web of Science, Scopus, Google Scholar, etc., this article provides the overview of the recent development of PVDF-based membranes during the recent several decades. The detailed information regarding PVDF as a polymer material as well as the main challenge in the development of PVDF-based membranes with bet.....

80 hits